Coating for cooling air holes

ABSTRACT

A method of repairing a component removes a prior coating from an underlying metal substrate. Small cooling air holes extend through the substrate and the coating that is to be removed. A new coating layer is placed on the metal substrate, and over the existing cooling air holes. The location of the cooling air holes is identified by inspecting the coated component for the location of indicators of the coating passing over the cooling air holes. The identified location of the indicators is used to control a cutting tool to remove any new coating from the cooling air holes. The basic method may also benefit new manufacture.

BACKGROUND OF THE INVENTION

This application relates to a method of repairing a coating on a component having small cooling air holes.

Gas turbine engines are known, and typically include a compressor delivering air into a combustion section where it is mixed with fuel and ignited. Products of this combustion pass downstream over turbine rotors, driving them to rotate. The turbine rotors typically include rotor drums carrying a plurality of blades. The blades are subjected to a great deal of heat, and thus air-cooling techniques have been developed for the turbine blades. In addition, there are typically static vanes positioned intermediate rows of the blades, and the static vanes are also provided with air-cooling techniques.

Other locations within a gas turbine engine also experience challenges from heat. As an example, structure in the combustion section may require air-cooling. In addition, components downstream of the turbine sections may also experience very high temperatures, and may be provided with air-cooling.

One standard air-cooling technique is a provision of a plurality of very small holes to direct cooling air from an internal cavity in the component to the outer surface of the component. Other ways of providing air to the holes would include supplying air from a plenum, or a pressurized air stream.

In addition, the components are typically provided with various coatings to assist in surviving the extreme challenges of the turbine environment. One such coating is a thermal barrier coating. The thermal barrier coatings have sometimes become distressed, such as experiencing spallation or liberation. The components are then typically recoated.

SUMMARY OF THE INVENTION

In one featured embodiment, a method of repairing a component includes the steps of removing a prior coating from an underlying metal substrate, there being small cooling air holes extending through the substrate and the coating that is to be removed, placing a new coating on the substrate, and over cooling air holes, identifying the location of the cooling air holes by inspecting the coated component for the location of indicators of the coating passing over the cooling air holes, and using the identified location of the indicators to control a cutting tool to remove coating from the cooling air holes.

In another embodiment according to the previous embodiment, the location of the indicators is captured by a vision system.

In another embodiment according to any of the previous embodiments, white light inspection is utilized as the vision system.

In another embodiment according to any of the previous embodiments, blue light inspection is utilized as the vision system.

In another embodiment according to any of the previous embodiments, laser scanning is utilized to identify the location of the indicators.

In another embodiment according to any of the previous embodiments, part probing is utilized to identify the location of the indicators.

In another embodiment according to any of the previous embodiments, the coating is removed from the cooling air holes using laser drilling.

In another embodiment according to any of the previous embodiments, the coating is removed from the cooling air holes using electron discharge machining.

In another embodiment according to any of the previous embodiments, the coating is removed from the cooling air holes in using a water drill.

In another embodiment according to any of the previous embodiments, the coating includes a bond layer directly deposited on the substrate and an outer coating deposited on the bond layer.

In another embodiment according to any of the previous embodiments, the outer coating is a thermal barrier coating.

In another embodiment according to any of the previous embodiments, the component is a gas turbine engine component having an airfoil, and internal air-cooling supply cavities to deliver air to the cooling air holes.

In another embodiment according to any of the previous embodiments, the coating is provided with a top coat to assist with the identification of the indicators, and the drilling.

In another embodiment according to any of the previous embodiments, the top coat is boron nitride.

In another featured embodiment, a method of coating a component includes the steps of placing a coating on a metal substrate, and over cooling air holes formed through the metal substrate, identifying the location of the cooling air holes by inspecting the coated component for the location of indicators of the coating passing over the cooling air holes, and using the identified location of the indicators to control a cutting tool to remove coating from the cooling air holes.

In another embodiment according to the previous embodiment, the location of the indicators is captured by a vision system.

In another embodiment according to any of the previous embodiments, one of white light inspection and blue light inspection is utilized as the vision system.

In another embodiment according to any of the previous embodiments, the coating includes a bond layer directly deposited on the substrate and an outer coating deposited on the bond layer.

In another embodiment according to any of the previous embodiments, the component is a gas turbine engine component having an airfoil, and internal air-cooling supply cavities to deliver air to the cooling air holes.

In another embodiment according to any of the previous embodiments, the coating is provided with a top coat to assist with the identification of the indicators, and the drilling.

These and other features of this application will be best understood from the following specification and drawings, the following of which is a brief description.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 shows a gas turbine engine component.

FIG. 2A shows a damaged coating on a component.

FIG. 2B shows a first step in repairing the component.

FIG. 2C shows a subsequent step.

FIG. 3 shows an intermediate product, consistent with the FIG. 2C step.

FIG. 4A shows a subsequent step.

FIG. 4B shows a final step.

DETAILED DESCRIPTION

FIG. 1 shows a component 20 which may typically be a gas turbine engine turbine blade or vane. The component has a coating, as known, and the coating has been distressed as shown schematically at 121. This may be the coating breaking away from the surface of the component 20, and may be a problem known as spallation or liberation. The coating may be a thermal barrier coating which is typically used to assist the component in surviving in the extreme temperatures faced during normal operation. However, other type coatings may benefit from the teaching of this application.

A plurality of cooling air holes 24 are shown in the component 20. As known, the component 20 has internal cavities, shown in phantom at 15. Those cavities receive air, as known, and may deliver the air outwardly to a skin of the component through the cooling air holes 24.

FIG. 2A shows a first step in repairing the coating on the component 20. As shown, the component 20 has a base metal 26, an outer bond layer 28 on the base metal, and the coating layer 30. The coating layer 30 may be a thermal barrier coating. As shown, cooling air holes 124 and 126 extend through both coating layers 28 and 30. For original equipment manufacture, the cooling air holes 124 and 126 may be cut through the coating layers 28 and 30, and the body 26 at the same time. As shown, there is a distressed area 121 which is requiring the component be recoated.

Holes used for this sort of function may be on the order of 0.020-0.050 inch (0.050 -0.127 cm). Holes such as hole 124, may be drilled normal to the surface, and may be angled in a range of 20-45 degrees.

Thus, as shown in FIG. 2B, a cleaning instrument, such as a water jet tool, shown schematically at 50, removes the coating layers 28 and 30. As shown, there is a “cleaned” area 52. Once the component has its entire coating 28 and 30 removed, subsequent bond coating 54 and a subsequent coating, such as the thermal barrier coating 56, are deposited on the metal body 26.

As can be appreciated from FIG. 2C, there will be dimples 58 associated with the coatings aligned with the openings 124 and 126 in the recoated component 120. These dimples provide an indication of the location of the underlying holes, but require removal before the component can be returned to operation.

The indicator, or dimples, may be generally volcano-shaped depressions in the coating. On the other hand, it is also possible that there will be a hole extending through the coating. That is, there may actually be a hole extending somewhat through the coating, however, there would still be coating in the complete cooling air hole that should be removed. These features are also indicators of the presence of an underlying hole.

FIG. 3 shows these dimples or other indicators 58 on the side of a component 120.

FIG. 4A shows the component 120 after the depositing of the coating as shown in FIG. 2C. As shown, there are a plurality of dimples or indicators 58 associated with the cooling air holes.

Some visual inspection technique will be utilized to determine the location of these dimples, or other indicators, of an underlying hole underneath the coating layers. This is shown as a visual camera 60 communicating with an appropriate electronic machine such as a computer 62. A map of the location of the dimples 58 is captured and stored in the computer 62. White light inspection, blue light inspection or other vision systems, laser scanning or simple or complex part probing may be utilized to capture the location of the dimples 58.

Once the location of the dimples is found, the holes are recut through the new coating as shown in FIG. 4B. A cutting tool, such as a water jet or laser 64 communicates with the computer 62 and utilizes the previously identified location of the indicators to control where to clean the holes as shown at 124. In addition, the newly captured location of the dimples may be utilized in combination with the known location where the holes were believed to have been formed initially.

The term “tool” is broadly intended in this application. As an example, the water jet or laser 64 would be a “tool.” Other tools may include mechanical means, including grinding or drilling. Also, abrasive techniques could be utilized, such as grit or sandblasting. Finally, electro-discharge machining is an option. All of these would come under the broad term “tool” as would other methods of removing the material.

By utilizing the inspection technique, the present invention is able to accurately drill the holes, without drilling at a location not including any hole, which would potentially ruin the new coating. In fact, the new holes need not be perfectly aligned with the original holes, but the method captures the majority of the original hole locations.

A top coat, such as boron nitride, or other thin coating, may be applied outwardly of the recoated component 120 to assist with the hole formation, and the optical inspection technique.

While the disclosed methods have primary application as repair techniques, there may be benefits for utilizing the inspection techniques for forming holes through a coating in a new manufacture.

A worker of ordinary skill in this art would recognize that certain modifications would come within the scope of this invention. For that reason, the following claims should be studied to determine the true scope and content of this invention. 

1. A method of repairing a component comprising the steps of: a) removing a prior coating from an underlying metal substrate, there being small cooling air holes extending through said substrate and said coating that is to be removed; b) placing a new coating on the substrate, and over cooling air holes; c) identifying the location of the cooling air holes by inspecting the coated component for the location of indicators of the coating passing over the cooling air holes; and d) using the identified location of the indicators to control a cutting tool to remove coating from the cooling air holes.
 2. The method as set forth in claim 1, wherein the location of the indicators is captured by a vision system.
 3. The method as set forth in claim 2, wherein white light inspection is utilized as the vision system.
 4. The method as set forth in claim 2, wherein blue light inspection is utilized as the vision system.
 5. The method as set forth in claim 1, wherein laser scanning is utilized to identify the location of the indicators.
 6. The method as set forth in claim 1, wherein part probing is utilized to identify the location of the indicators.
 7. The method as set forth in claim 1, wherein the coating is removed from the cooling air holes in step d) using laser drilling.
 8. The method as set forth in claim 1, wherein the coating is removed from the cooling air holes in step d) using electron discharge machining.
 9. The method as set forth in claim 1, wherein the coating is removed from the cooling air holes in step d) using a water drill.
 10. The method as set forth in claim 1, wherein said coating includes a bond layer directly deposited on the substrate and an outer coating deposited on the bond layer in step b).
 11. The method as set forth in claim 10, wherein said outer coating is a thermal barrier coating.
 12. The method as set forth in claim 1, wherein said component is a gas turbine engine component having an airfoil, and internal air-cooling supply cavities to deliver air to the cooling air holes.
 13. The method as set forth in claim 1, wherein the coating is provided with a top coat to assist with the identification of the indicators, and the drilling.
 14. The method as set forth in claim 13, wherein said top coat is boron nitride.
 15. A method of coating a component comprising the steps of: a) placing a coating on a metal substrate, and over cooling air holes formed through said metal substrate; b) identifying the location of the cooling air holes by inspecting the coated component for the location of indicators of the coating passing over the cooling air holes; and c) using the identified location of the indicators to control a cutting tool to remove coating from the cooling air holes.
 16. The method as set forth in claim 15, wherein the location of the indicators is captured by a vision system.
 17. The method as set forth in claim 16, wherein one of white light inspection and blue light inspection is utilized as the vision system.
 18. The method as set forth in claim 15, wherein said coating includes a bond layer directly deposited on the substrate and an outer coating deposited on the bond layer in step b).
 19. The method as set forth in claim 15, wherein said component is a gas turbine engine component having an airfoil, and internal air-cooling supply cavities to deliver air to the cooling air holes.
 20. The method as set forth in claim 15, wherein the coating is provided with a top coat to assist with the identification of the indicators, and the drilling. 